The aim of this study was to test the hypothesis that there is a direct relationship between surface structure and tensile strength of orthodontic alloys submitted to different levels of welding current. Three types of alloys were assessed. One hundred and eight cross-sectional test specimens ("X") were made, 18 for each wire combination, and divided into 6 groups: SS (steel-steel); SN (steel-NiTi); SB (steel-Beta-Ti); NN (NiTi-NiTi); NB (NiTi-Beta-Ti) and BB (Beta-Ti-Beta-Ti), submitted to 6 spot-welding procedures at different levels of current (Super Micro Ponto 3000). Student-Newman-Keuls, Wilcoxon signed-rank, and Kruskal-Wallis tests were used (p < .05). Statistical difference was found between SN group and all the other alloy combinations (p < .05). Initial roughness of alloys ranged from .04 to .55 Ra, with statistical difference between groups (p < .001). The hypothesis was rejected and the tensile strength of Ti-alloys combinations Steel × Beta-Ti was significantly affected by the current level at P50, which changed the properties and structure of the wires.

OBJETIVO: avaliar por meio de Tomografia Computadorizada Cone-Beam (TCCB) os efeitos transversais, imediatos e após o período de contenção, da expansão rápida da maxila (ERM) em pacientes com má oclusão de Classe II. MÉTODOS: dezessete crianças (idade inicial média de 10,36 anos) com má oclusão de Classe II e deficiência transversal esquelética da maxila foram submetidas ao protocolo de ERM com aparelho expansor de Haas. TCCBs foram realizadas antes dos procedimentos clínicos (T1), imediatamente após a estabilização do parafuso expansor (T2) e após completados 6 meses de contenção e removido o aparelho (T3). Com o software Dolphin, foram possíveis a manipulação das imagens e as mensurações. O teste t de Student pareado foi utilizado para identificar significância estatística (p<0,05) entre os intervalos T2 e T1, T3 e T2, e T3 e T1. RESULTADOS: imediatamente após a ERM, ocorreu aumento significativo da largura maxilar basal, alveolar e dentária de 1,95mm, 4,30mm e 6,89mm, respectivamente, e inclinação vestibular dos primeiros molares direito (7,31º) e esquerdo (6,46º). Ao final do período de contenção, o aumento transversal foi mantido e a inclinação dentoalveolar retornou ao valor inicial. CONCLUSÕES: a ERM foi efetiva no aumento da dimensão transversa da maxila, tanto esquelético quanto dentário, sem causar inclinação dos molares de ancoragem em pacientes com má oclusão de Classe II.

OBJECTIVE: The aim of this study was to evaluate by Cone-Beam Computed Tomography (CBCT) transversal responses, immediately and after the retention period, to rapid maxillary expansion (RME), in Class II malocclusion patients. METHODS: Seventeen children (mean initial age of 10.36 years), with Class II malocclusion and skeletal constricted maxilla, underwent Haas´ protocol for RME. CBCT scans were taken before treatment (T1), at the end of the active expansion phase (T2) and after the retention period of six months (T3). The scans were managed in Dolphin software, where landmarks were marked and measured, on a coronal slice passing through the upper first molar. The paired Student´s t-test was used to identify significant differences (p<0.05) between T2 and T1, T3 and T2, and T3 and T1. RESULTS: Immediately after RME, the mean increase in maxillary basal, alveolar and dental width was 1.95 mm, 4.30 mm and 6.89 mm, respectively. This was accompanied by buccal inclination of the right (7.31°) and left (6.46°) first molars. At the end of the retention period, the entire transverse dimension increased was maintained and the dentoalveolar inclination resumed. CONCLUSIONS: The RME therapy was an effective procedure to increase transverse maxillary dimensions, at both skeletal and dentoalveolar levels, without causing inclination on anchorage molars in Class II malocclusion patients with skeletal constricted maxilla.

O objetivo deste estudo foi testar a hipótese que não há diferença no desempenho dos cimentos de ionômero de vidro reforçados com resina entre si quanto à liberação de flúor antes e após recarga com flúor. Os materiais foram divididos em 5 grupos: 2 cimentos de ionômero de vidro reforçados com resina utilizados para cimentação de bandas ortodônticas: Grupo FOB (Fuji Ortho Band) e Grupo MCB (Multi-Cure Glass Ionomer Orthodontic Band Cement); 2 cimentos de ionômero de vidro reforçados com resina e 1 compósito utilizados para colagem de bráquetes ortodônticos: Grupo OGLC (Ortho Glass LC), Grupo FOLC (Fuji Ortho LC); e Grupo TXT (Transbond XT), respectivamente. A liberação de flúor foi medida durante 60 dias, através de eletrodo íon seletivo conectado a um analisador de íons. Após 4 semanas, os corpos de prova foram expostos a solução de fluoreto de sódio à 0,221%. Os resultados evidenciaram que os cimentos atingiram o pico máximo de liberação de flúor com 24 h após presa inicial. Não houve diferença estatisticamente significante entre a quantidade de flúor liberado após as recargas de fluoreto de sódio entre os grupos FOB e OGLC do 31° ao 36° dia (p>0.05). Concluindo os cimentos FOB e OGLC apresentaram maior capacidade de captação e liberação de flúor comparada aos outros CIVRRs.

The aim of this study was to test the hypothesis that there is no difference in the fluoride release behavior of resin-reinforced glass ionomer cements before or after fluoride recharge. The materials were divided into 5 groups: 2 resin-reinforced glass ionomer cements used for attaching orthodontic bands, that is, group FOB (Fuji Ortho Band) and group MCB (Multi-Cure Glass Ionomer Orthodontic Band Cement); 2 resin-reinforced glass ionomer cements and a composite used for bonding orthodontic brackets, that is, group OGLC (Ortho Glass LC), group FOLC (Fuji Ortho LC), and group TXT (Transbond XT), respectively. Fluoride release was measured during a 60-day period by using selective ion electrodes connected to an ionic analyser. After 4 weeks, the samples were exposed to 0.221% sodium fluoride solution. The results showed that cements achieved a maximum fluoride release 24 h after initial setting. No statistically significant differences were observed between groups FOB and OGLC regarding the amount of released fluoride following fluoride recharge from day 31 to day 36 (p>0.05). In conclusion, FOB and OGLC cements showed a higher capacity of capturing and releasing fluoride compared to the other cements studied.

OBJETIVOS: o objetivo do presente trabalho é avaliar a deformação e fratura de mini-implantes ortodônticos de diferentes marcas comerciais submetidos ao carregamento na direção perpendicular ao seu comprimento. METODOLOGIA: foram utilizados 75 mini-implantes divididos em cinco grupos (n = 15): M (Mondeal, Tuttlingen, Germany), N (Neodent, Curitiba, Brasil), I (INP, São Paulo, Brasil), S (SIN, São Paulo, Brasil) e T (Titanium Fix, São José dos Campos, Brasil). Os mesmo foram inseridos perpendicularmente em osso cortical suíno e levados à máquina universal de ensaios mecânicos Emic DL 10.000, a uma velocidade de 0,5mm por minuto. Foi avaliada a força necessária para deformar os mini-implantes em 0,5, 1, 1,5, 2mm e para fratura. Os dados foram analisados pela análise da variância (ANOVA) e teste de Tukey. RESULTADOS: os mini-implantes do grupo S necessitaram força maior para que ocorresse deformação e fratura, esses resultados foram estatisticamente significativos em relação aos demais (p < 0,05), que se deformaram e fraturaram com força menor. O grupo M apresentou os menores valores para deformar, entretanto, sem diferença estatística com o grupo N (p > 0,05). Para fraturar, o grupo T apresentou os menores valores, com diferença estatística com os grupos M, S e I. CONCLUSÕES: pode-se concluir que o formato do mini-implante está diretamente relacionado com sua resistência. Apesar de diferenças existentes quanto à resistência entre eles, todos se mostraram aptos para a utilização clínica.

OBJECTIVE: The objective of the present study is to assess both deformation and fracture of orthodontic mini-implants of different trade marks by submitting them to loads perpendicularly applied along their lengths. METHODS: A total of 75 mini-implants were divided into five groups (n = 15) according to their manufacturers: group M (Mondeal, Tuttlingen, Germany), group N (Neodent, Curitiba, Brazil), group I (INP, São Paulo, Brazil), group S (SIN, São Paulo, Brazil), and group F (Titanium Fix, São José dos Campos, Brazil). The mini-implants were perpendicularly inserted into swine cortical bones and then submitted to mechanical tests by using a universal testing machine (Emic DL 10.000) at cross-head speed of 0.5mm/min. The force required for deforming and fracturing the mini-implants at 0.5, 1.0, and 2.0mm was assessed. Data were assessed by using variance analysis (ANOVA) and Tukey's test. RESULTS: Mini-implants of group S were found to need higher forces to be deformed and fractured in comparison with other groups whose mini-implants were submitted to lower forces, a result that is statistically significant (p < 0.05). Group M showed the lowest values regarding deformation with no statistical difference compared to group N (p > 0.05), whereas group T had the lowest values regarding fracture with statistical differences compared to groups M, S, and I. CONCLUSIONS: Based on the present study, one can conclude that the shape of the mini-implants is directly related to their flexural strength. Despite the differences reported above, the mini-implants were found to be clinically useful.